Product name

Cracking paste    咨詢電話：13713145387陳秋婷   QQ：1747383364

State

Paste

Packing

25KG/drum for white,  20KG/drum for clear

Storage

6 months in cool place

Application

Suitable for knitting

Features

1. High fastness

2. High softness

3. SGS detecting passed, no PVC, no heavy metal, no NPEOs.

Mix proportion

Light: White cracking paste 70-100% + Clear cracking paste 0-30% + pigment ?% + fixing agent 2%

Deep: White cracking paste 20-30% + Clear cracking paste 70-80% + pigment ?% + fixing agent 2%

Printing process

1. Printing with clear cracking paste ( for underbase) for 1-2 times

2. Mixing with white cracking paste, clear cracking paste, pigment, fixing agent and stirring them evenly.

3. Printing again for 2-3 times (3-4 scrapes per time).

4. Drying the paste surface with cold air, it will be cracked by itself after it’s dry.

5. Hot pressing the printing for about 5 seconds with 150℃ to make it better adhesion.

6. Finish. 

Attentions

1. Thick screen is suggested for the best effect (print for 1 time only).  If with thin screen,  please printing for 2-3 times, and blow the paste surface with cold air to dry it fast and re-printing before it’s cracked.

2. Please take the fabric up after it’s completely cracked, otherwise it’s won’t be cracked naturally.

3. More clear and thinner the paste is , thinner the crack is.

4. The pigment can not be exceeded in 12%, otherwise it'll be easily faded. 

品名

特軟龜裂漿          咨詢電話：13713145387陳秋婷  QQ：1747383364

外觀

糊狀

包裝

白膠漿25KG/桶，透明漿20KG/桶，打底透明漿20KG/桶

貯存期

常溫下6個月

應用

針織布

調(diào)配比例

印淺色：龜裂白膠漿70-100% +龜裂透明漿0-30% + 色漿？% + 固化劑2%

印深色：龜裂白膠漿20-30% + 龜裂透明漿70-80% + 色漿？% + 固化劑2%

賣點

1. 可耐正常水洗

2. 手感柔軟

工藝流程

1. 絲網(wǎng)選用80-100目，用絲印硬方刀75度刮印，先用龜裂打底透明漿打底+固化劑印1-2次,

第一板用力刮4-6刀，

2. 將龜裂白膠漿，透明漿，色漿，固化劑攪拌均勻印2-3次（每次刮3-4刀）

3. 自然干燥爆裂（要在臺板上面自然爆裂，要使用粘性好的臺板膠，靠張力去自然爆裂的）

4. 起布（必須完全爆裂后才能起布，因為起布后不會再自然爆裂）

注意事項

1. 龜裂漿一定要配打底透明漿使用，否則易脫落且沒有彈力；

2. 若膠漿印前太稠可加水，切勿加固漿以免影響爆裂效果；

3. 建議曬厚網(wǎng)印龜裂漿,一次印夠色為最佳.若用薄網(wǎng)印刷,請用冷風吹漿層的表面,在漿層還沒有裂開之前返印；(裂紋的大小與多少可以在龜裂白和龜裂透明的互配比例和印出來的漿層厚薄控制,龜裂透明比例越多和印出來的漿層越薄它的裂紋就越細,反之它的裂紋越粗。

4.起布之后建議過熱壓燙一下，防止翹邊。